| Grade |
P1000 series |
P2000 series |
P3000 series |
P4000 series |
| Application |
Injection molding |
Sheet |
Film |
Fiber |
* We have many kinds of special grades except upper basics grades (Please contact our Customer Center for details.)
| Property |
Unit |
ABS |
PLA |
Pureco (P1000) |
Pureco (P1100) |
ASTM Method |
| Specific Gravity |
g/cm³ |
1.05 |
1.24 |
1.22 |
1.29 |
D792 |
| Melt Flow Rate |
g/10min |
8 |
11 |
14 |
12 |
D1238 (190℃, 2.16kg) |
| Clarity |
O/△/X |
X |
O |
△ |
X |
- |
| Tensile Strength |
MPa |
40 |
62 |
55 |
60 |
D638 |
| Tensile Elongation |
% |
30 |
4 |
50 | 30 |
D638 |
| Flexural Strength | MPa |
60 |
108 |
50 |
120 |
D790 |
| Flexural Modulus | MPa |
2200 |
3600 |
2200 |
3700 |
D790 |
| Notched Izod Impact |
J/m |
150 |
16 |
200 |
150 |
D256 |
| Heat Distortion Temperature |
℃ | 89 | 55 | 110 | 130 | E2092 (0.45MPa) |
* This data is as a result of using high temperature moulding(90℃), so it is typical properties; not to be construed as specifications.
| Property |
Unit |
HIPS |
PLA |
Pureco (P2000) |
Pureco (P2100) |
ASTM Method |
| Specific Gravity |
g/cm³ |
1.03 |
1.24 |
1.22 |
1.28 |
D792 |
| Melt Flow Rate | g/10min |
4 |
2.5 |
6 |
4 |
D1238 (190℃, 2.16kg) |
| Clarity |
O/△/X |
O |
O |
△ |
X |
- |
| Tensile Strength | MPa |
28 |
53 |
50 |
55 |
D638 |
| Tensile Modulus | MPa |
1800 |
3500 |
3000 |
3600 |
D638 |
| Tensile Elongation | % |
50 |
6 |
40 |
20 |
D638 |
| Flexural Strength | MPa |
48 |
110 |
50 |
120 |
D790 |
| Flexural Modulus | MPa |
2200 |
3600 |
2200 |
3700 |
D790 |
| Notched Izod Impact |
J/m |
80 |
16 |
180 |
140 |
D256 |
| Heat Distortion Temperature |
℃ | 92 | 55 | 110 | 130 | E2092 (0.45MPa) |
* This data is as a result of using high temperature moulding(90℃), so it is typical properties; not to be construed as specifications.